Abstract
In this study, the properties of vinyl ester/glass flake (VE/GF) coating on mild steel plates was investigated to determine its anti-corrosion performance. The corrosion penetration rate of VE/GF coated and uncoated mild steel was evaluated using immersion tests for 20 days. Corrosion resistance of the coating was evaluated in various corrosive environments viz. 5 % HCl, 8 % HCl, 5 % NaOH and 7 % NaOH. The mild steel plates were coated with four different thicknesses of VE/GF coating and a comparative analysis was carried out to evaluate the corrosion protection efficiency. Scanning electron microscopy was carried out before and after the immersion test to study the morphological changes and products of corrosion.
| Original language | English |
|---|---|
| Pages (from-to) | 1227-1229 |
| Number of pages | 3 |
| Journal | International Journal of Materials Research |
| Volume | 105 |
| Issue number | 12 |
| DOIs | |
| Publication status | Published - Dec 1 2014 |
| Externally published | Yes |
Fingerprint
Keywords
- Anti-corrosion performance
- Coatings
- Immersion test
- Vinyl ester/glass flake
ASJC Scopus subject areas
- Metals and Alloys
- Materials Chemistry
- Condensed Matter Physics
- Physical and Theoretical Chemistry
Cite this
Anticorrosion behaviour of VE/GF coatings on mild steel. / Barbhuiya, Salim; Choudhury, Ikbal; Memon, Shazim.
In: International Journal of Materials Research, Vol. 105, No. 12, 01.12.2014, p. 1227-1229.Research output: Contribution to journal › Article
}
TY - JOUR
T1 - Anticorrosion behaviour of VE/GF coatings on mild steel
AU - Barbhuiya, Salim
AU - Choudhury, Ikbal
AU - Memon, Shazim
PY - 2014/12/1
Y1 - 2014/12/1
N2 - In this study, the properties of vinyl ester/glass flake (VE/GF) coating on mild steel plates was investigated to determine its anti-corrosion performance. The corrosion penetration rate of VE/GF coated and uncoated mild steel was evaluated using immersion tests for 20 days. Corrosion resistance of the coating was evaluated in various corrosive environments viz. 5 % HCl, 8 % HCl, 5 % NaOH and 7 % NaOH. The mild steel plates were coated with four different thicknesses of VE/GF coating and a comparative analysis was carried out to evaluate the corrosion protection efficiency. Scanning electron microscopy was carried out before and after the immersion test to study the morphological changes and products of corrosion.
AB - In this study, the properties of vinyl ester/glass flake (VE/GF) coating on mild steel plates was investigated to determine its anti-corrosion performance. The corrosion penetration rate of VE/GF coated and uncoated mild steel was evaluated using immersion tests for 20 days. Corrosion resistance of the coating was evaluated in various corrosive environments viz. 5 % HCl, 8 % HCl, 5 % NaOH and 7 % NaOH. The mild steel plates were coated with four different thicknesses of VE/GF coating and a comparative analysis was carried out to evaluate the corrosion protection efficiency. Scanning electron microscopy was carried out before and after the immersion test to study the morphological changes and products of corrosion.
KW - Anti-corrosion performance
KW - Coatings
KW - Immersion test
KW - Vinyl ester/glass flake
UR - http://www.scopus.com/inward/record.url?scp=84918544398&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=84918544398&partnerID=8YFLogxK
U2 - 10.3139/146.111133
DO - 10.3139/146.111133
M3 - Article
VL - 105
SP - 1227
EP - 1229
JO - International Journal of Materials Research
JF - International Journal of Materials Research
SN - 1862-5282
IS - 12
ER -